DERAKANE 411-350 epoxy vinyl ester resin is based on bisphenol-A epoxy resin and has become the"industry standard" due to its wide range of end-use applications and ability to be used in a wide range of fabrication techniques.
DERAKANE 411-350 epoxy vinyl ester resin is based on bisphenol-A epoxy resin and has become the"industry standard" due to its wide range of end-use applications and ability to be used in a wide range of fabrication techniques.
Property | Value (SI) | Method | Value (US) | Method |
Tensile Strength | 86 MPa | ISO 527 | 12000 psi | ASTM D638 |
Tensile Modulus | 3200 MPa | ISO 527 | 460 kpsi | ASTM D638 |
Tensile Elongation at Yield | 5-6% | ISO 527 | 5-6% | ASTM D638 |
Flexural Strength | 150 MPa | ISO 178 | 22000 psi | ASTM D790 |
Flexural Modulus | 3400 MPa | ISO 178 | 490 kpsi | ASTM D790 |
Heat Distortion Temperature | 105 °C | ISO 75 | 220 °F | ASTM D648 |
Glass Transition Temperature, Tg² | 120 °C | ISO 11359-2 | 250 °F | ASTMD3419 |
Volume Shrinkage | 7.8 % | 7.8 % | ||
Barcol Hardness | 35 | EN 59 | 35 | ASTM D2583 |
Density | 1.14 g/cm3 | ISO 1183 | ASTM D792 |
Application
-DERAKANE 411-350 resin is designed for use in fabricating FRP storage tanks, vessels, ducts and on-site maintenance projects, paticularly in chemical processing and pulp and paper operations.
- The resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding, compression molding and resin transfer molding techniques, pultrusion and molded grating applications.
- An alternate viscosity, optimized for some vacuum infusion processes is available as DERAKANE MOMENTUM 411-200 resin.
- An alternate for low styrene content (HAP) is available as DERAKANE 441-400 resin.